Product details
Model Number: ZXL040
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steel with Mn, Cr and MoApplicationsThrough-hardenableRoller bearingsChemical composition (in weight%)
C: 0.97
Si: 0.50
Mn: 0.95
Cr: 1.93
Mo: 0.55
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing
Heat to approx 750℃, cool slowly
This will produce a maximum Brinell hardness of 217
Hardening
Harden from a temperature of 800-850℃followed by oil quenching
Hardness after quenching is approx 59 HRC
Tempering
Tempering temperature: 100 to 250℃
Forging
Hot forming temperature: 1050 to 850℃
Specifications:
Grade: material number 1.3539
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’srequirements
Delivery: 7-20 days after received deposit of T/T
C: 0.97
Si: 0.50
Mn: 0.95
Cr: 1.93
Mo: 0.55
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing
Heat to approx 750℃, cool slowly
This will produce a maximum Brinell hardness of 217
Hardening
Harden from a temperature of 800-850℃followed by oil quenching
Hardness after quenching is approx 59 HRC
Tempering
Tempering temperature: 100 to 250℃
Forging
Hot forming temperature: 1050 to 850℃
Specifications:
Grade: material number 1.3539
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’srequirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe